It is nitriding steel that is added Al. Cr. in nitriding treatment to possess superior fatigue strength, surface hardness and wear-resistance, so it can be used to produce high-precision mechanical parts.
Cylinder liner, compressor parts, hydraulic parts,…etc.
Standard Code | Spec No. | Material No. | Mark |
---|---|---|---|
CNS | 4444 | SACM645 | |
JIS | G4202 | SACM645 | |
DIN | 17211 | 1.8507 | 34CrAl-Mo5 |
ASTM | A355 | Class A | |
DIN | 17211 | 1.8509 | 41CrAlMo7 |
(C)% | (Si)% | (Mn)% | (P)% | (S)% | (Ni)% | (Cr)% | (Mo)% | (Al)% | Thickness(mm) | Yield strength(Mpa) | Tensile strength(Mpa) | Elongation(%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|
0.4~0.5 | 0.15~0.5 | ≦ 0.6 | ≦ 0.03 | ≦ 0.03 | ≦ 0.25 | 1.3~1.7 | 0.15~0.3 | 0.7~1.2 | ||||
0.4~0.5 | 0.15~0.5 | ≦ 0.6 | ≦ 0.03 | ≦ 0.03 | ≦ 0.25 | 1.3~1.7 | 0.15~0.3 | 0.7~1.2 | ||||
0.3~0.27 | 0.2~0.5 | 0.5~0.8 | ≦ 0.03 | ≦ 0.035 | 1~1.3 | 0.15~0.25 | 0.8~1.2 | ≦ 70 | ≧ 590 | 780~980 | ≧ 14 | |
0.38~0.43 | 0.15~0.35 | 0.5~0.7 | ≦ 0.035 | ≦ 0.04 | 1.4~1.8 | 0.3~0.4 | 0.95~1.3 | |||||
0.38~0.45 | 0.2~0.5 | 0.5~0.8 | ≦ 0.03 | ≦ 0.025 | 1.5~1.8 | 0.25~0.4 | 0.8~1.2 | ≦ 100 | ≧ 735 | 930~1,130 | ≧ 12 |